AISI E2512 SAE J1249 DIN 1.5681 Stainless Steel Rod

China SHANGHAI UNITE STEEL certification
China SHANGHAI UNITE STEEL certification
I'm Online Chat Now

AISI E2512 SAE J1249 DIN 1.5681 Stainless Steel Rod

large.img.alt
small.img.alt small.img.alt

Large Image :  AISI E2512 SAE J1249 DIN 1.5681 Stainless Steel Rod

Product Details:
Place of Origin: CHINA
Brand Name: UST
Certification: ISO9001
Model Number: DIN 1 5681
Payment & Shipping Terms:
Minimum Order Quantity: MOQ1-2TONS
Packaging Details: Wooden packages
Delivery Time: 4-6 weeks
Payment Terms: L/C, T/T
Supply Ability: 800 ton/month
Detailed Product Description
Standard: ASTM,AISI,DIN,JIS,EN Application: Industry
Certification: ISO,BV,SGS Packing: Standard Seaworthy Package,In Wooden Cases(for FCL/ LCL Shipment)
Main Market: Europe,Africa,Asia,The Americas
High Light:

DIN 1.5681 Stainless Steel Rod

,

AISI E2512 Stainless Steel Rod

grade AISI E2512 SAE J1249 DIN 1 5681 Bars

 

 

Product Details

 

Chemical composition % of the ladle analysis of grade AISI E2512 SAE J1249 / DIN 1.5681 Bars and Standards

 
C(%): 0.09~0.14
Si(%): 0.20~0.35
Mn(%): 0.45~0.60
P(%)≤: 0.025
S(%)≤: 0.025
Cr(%): -
Ni(%): 4.75~5.25

 

 

Machining performance
 
AISI E2512 the mechanical properties of the report, the report provides detailed performance analysis and application.
 
 
Machinability
 
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
 
Heat Treatment
 
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
 
Welding
 
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
 
Forging
 
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

 