Payment & Shipping Terms:
|Product Name:||Hot Forged Ring||Material:||Alloy Steel Ring|
|Surface::||Black, Bright And Polished||UT::||ASTM A 388 Or According To Customers' Requirement|
|Inspection::||The Third Party Is Acceptable||Certificate:||ISO9001-2008|
Forging Stainless Steel,
Steel Forged Rings
EN36A/15NiCr13/X3312H high-quality hot forged steel rings
EN36 is an alloy case hardening steel. Characteristics of the steel are toughness arising from the use of nickel and a more uniform hardness produced by the use of chromium. It is specifically designed for carburising to give a very hard case with a strong core.
Heavy Duty Bushings, Collets, Conveyor Pins, Heavy Duty Gears, King Pins, Ring Gears, Sprockets, Shafts, heavy-duty gears, collets etc. Or can be used for high tensile applications uncarburised but through hardened and tempered.
Australia AS 1444-1996-X3312/X3312H
Germany W.Nr 1.5752 DIN 14NiCr14
Great Britain BS970: PART 3: 1991 655 M13
BS970: 1955 - EN36A
EN10084-1998 1.5752 15NiCr13 or
Japan JISG 4052 SNC815H
JISG 4102 SNC815
U.S.A. SAE 3310 9310
AISI E3310 E9310
Phosphorous 0.04 max
Sulphur 0.04 max
Process: EAF+LF+VD+Forged+Heat Treatment(optional)
OD up to 8,000mm; ID up to 7,800mm; Thickness up to 500mm
Black, Peeled (K12), Turned & Polished (H10, H11)
Ultrasonic test :ASTM A 388 or according to customers' requirement
Heat to 890°C/920°C and soak for the necessary time to obtain the desired carburised depth.
Single Quench Treatment:
Heat the carburised parts to 800/820°C and quench in oil.
Double Quench Treatment:
Heat the carburised parts to 850/880°C, cool in oil or air then re heat to 760/780C and quench in oil.
After hardening temper at 150°C for 2 hours minimum, and allow to cool in air to give a final surface hardness in the region of Rockwell C60/62.
Certificate of Quality: issued in English, in addition the normal terms, production process, the mechanical property (yield strength, tensile strength, elongation and hardness), forged ratio, UT test result, Grain size, heat treatment methods and the sample of is shown on the Certificate of Quality.
Marking: Heat No. will be cold stamped and Steel grade, diameter (mm), length (mm), and the manufacturer LOGO and weight (kg) is painted