|Matrial:||Alloy Steel||Standard:||GB, ASTM, DIN,JIS|
|Grade:||4130 / 25CrMo4||Diameter:||4-1600mm|
|Length:||Below 16 Meters||Shape:||Round Bar|
|Techniques:||Cold Drawn; Hot Rolled; Cold Rolled; Forged||Surface:||Black, Bright, Polished, Peeled, Or Upon Request|
|Ultrasonic Test:||100% UT Passed||Processing:||Annealed Or Quenched And Tempered Provided|
|End:||Beveled, Plain End As Required||Quality Inspection:||SGS, BV Etc.|
|Service:||Cutting Service And 3rd Party Inspection Is Provided|
hot rolled round bar,
spring steel round bar
AISI 4130 alloy steel is a medium carbon, low alloy steel in ASTM A29 standard. ASTM 4140 steel is also commonly referred to as a chromoly steel, or chrome moly steel, containing nominally 0.28-0.33% Carbon, 0.8-1.1% Chromium and 0.15-0.25% Molybdenum. It is similar to 4140 steel which has a higher carbon level (0.28-0.33%), giving 4130 material improved weldability, at the expense of through thickness strength. With the proper heat treatment it is also readily machined. Annealing ASTM 4130 alloy steel offers excellent ductility. AISI 4130 steel is usually supplied as round bar commonly in the hardened and tempered condition.
AISI/SAE 4130 steel grade is a versatile alloy with good atmospheric corrosion resistance and reasonable strength up to around 315º C (600º F). It shows good overall combinations of strength, toughness and fatigue strength.
AISI 4130 steel alloy is used primarily in the construction of commercial and military aircraft and ground support systems. Alloy steel 4130 is an intermediate strength material. Lighter gauges offer lighter weight but still maintain great strength, making it excellent for auto racing and aerospace. This low alloy 4130 steel is widely used in many applications, and some typical application areas are as follows:
Cold drawn: 4-100 mm
Peeled: 30-160 mm
Grinded: 4- 600 mm
Turned: 130-1200 mm
Hot rolled: 12-320 mm
Hot forged: 130-1600 mm
-EAF+(ESR) or EAF+LF+VD+(ESR)
-HOT rolled; Cold rolled; Forged; Cold Drawn
-Heat Treatment: Untreated, Annealing, N+T, Q+T
-Smelting: EAF+LF+VD (+ESR)
-Surface Finish: Black, Rough Machined, Peeled, Turned or upon request
-UT 100% passed
-Cutting service provided
-Third Party inspection is acceptable (SGS, BV etc.)
AISI 4130 Steel Specification and Relevant Standards
|Standard||ASTM A29||EN 10250/EN10083||BS 970||JIS G4105|
ASTM 4130 Steels And Equilvalents Chemical Composition
AISI Alloy 4130 Steel Mechanical Properties
|Standard||Steel Grade||Yield strength σs/MPa (>=)||Tensile strength σb/MPa (>=)||
|Reduction of area ψ/% (>=)||Impact absorbing energy Aku2/J (>=)||HardnessVickers max|
Forging of 4130 Alloy Steel
ASTM A29 Grade 4130 steel should be forged between 1230 and 950 º C (2250 and 1750 º F). The lower the finishing temperature from forging, the finer will be the grain size. If the 4130 alloy steel is forged at too low a temperature, there is a risk of the formation of a non-uniform structure in certain areas of the forged part, necessitating a normalizing treatment, prior to further heat treatment.
AISI 4130 Steel Grade Heat Treatment
Annealing of 4130 steel forgings may be carried out by transferring the part straight from the forging operation to a furnace held at a suitable temperature, around 860º C (1575 º F) for annealing, holding for a suitable time then furnace cooling. In this way a structure suitable for machining may be obtained. This treatment is best used for parts with simple shapes. If the 4130 forging is such that some sections will finish much colder than others then a uniform structure will not be obtained and for best results a spheroidizing anneal at around 750 º C (1380 º F) may be used. It is safe to say that experience alone will decide the best type of annealing treatment to be used prior to machining.
It should then be cooled in the furnace at a rate of less than 50 F per hour down to 900 F, followed by air cooling from 900 F.
The nominal normalizing temperature for 4130 is 900 º C (1650 º F) followed by the 1600 F soak and oil quench, but production experience may necessitate a temperature either 50 º F (10 º C) above or below this figure. In fact when forgings are normalized before, for example, carburizing or hardening and tempering, the upper range of normalizing temperatures is used. When normalizing is the final heat treatment, the lower temperature range is used.
The steel 4130 should be austenitized – i.e. all micro constituents transformed to austenite – at 1500 to 1600 º F (815 to 870 º C). The actual austenitizing temperature is a function of chemical composition within the analysis range, section size and cooling method. Smaller sections of 4130 might be quenched in oil, heavier sections in water.
The actual tempering temperature will depend on what required properties are needed. Alloy steel 4130 is tempered at between 398 ºC -565 ºC (750 F and 1050 F), depending upon the strength level desired. The lower the tempering temperature the greater the strength. However, tempering should not be carried out between 200 – 420 ºC (400 – 790 º F) to avoid the danger of embrittlement.
The AISI 4130 alloy is readily machinable by conventional methods. Simple shapes might be machined following a normalizing treatment, whereas more complex shapes will require annealing. However, machining becomes difficult when the hardness of the 4130 steel is increased.
AISI 4130 steel is also good in weldability, and the 4130 alloy may be welded by any commercial method. The material may require a post-weld stress relief heat treatment in certain instances.
Low-hydrogen electrodes are recommended together with preheat at 150 – 260 º C (300 – 500 º F) to be maintained during welding, Cool slowly and stress relieve where possible.
What we can offer?
-We offer a wide range of steel products in a wide variety of dimensions and executions, according to the common international specifications or customize.
-Machining and heat treatment are available.
-Also, we advise you in choosing the right materials.
OUR MAIN PRODUCTS ARE LISTED AS BELOW
-Round: Dia. 4 -1600 mm
-Flat: T. 10-120 mm x W. 60-810 mm
-Block: T. 80-1200 mm x W. 100-1600 mm
PAYMENT AND SHIPPING
1. Both T/T and L/C will be acceptable
2. Trade Terms: FOB, CIF, CFR
3. The delivery will be in 10-15 days if have stock; For customized items, the delivery will be negotiated by both parties
4. Shipping by sea freight from Shanghai Port (PRC) for Bulk orders, by airfreight or express for samples
Shanghai Unite Steel Trading Co., Ltd
We are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.
In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china.
What’s more, we have built long, deep and close business relationship with dozens of steel company, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!
Q: Are you a manufacturer or merely a trader?
A: We are group of companies and owned manufacturer bases and trading company. We specialized in special steel which include alloy structural steel and carbon steel and stainless steel, etc. All material are with high quality and competitive price.
Q: How do you guarantee the quality of your product?
A: Firstly, we can provide the certificates from the third party, such as TUV, CE, if you need. Secondly, we have a complete set of inspection system and every process is checked by QC. Quality is the lifeline of enterprise survival.
Q: Delivery time?
A: We have ready stock for most of material grades in our warehouse. If the material doesn't have stock, the delivery lead time is about 5-30 days after receiving your prepayment or firm order.
Q: What is the payment term?
A: T/T or L/C.
Q: Can we visit your company and factory?
A: Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.
We are happy to answer your questions and make you an offer for these and other materials. Contact us now for more information.
Your Contact Person
Ms Chilli Ho
Contact Person: Eric
Product name: 826M40 Hot Rolle Steel Bar,Alloy Steel Round Bar With Peeled& Turned Surface, Size 10-350mm, Quenched & Tempered
Material grade: X9940/EN26/40NiCrMo10 4/DIN1.6745/826M40
Delivery condition: hot rolled/cold drawn/annealed/quenched&temperd
Surface condition: black surface/peeled/polished/turned/rough turned